nm500 plate thickness size price is expected to continue to fluctuate and rise in the near future

The company specializes in the research and development, production and sales of NM500 plate thickness size seamless pipes, longitudinally welded pipes, large-diameter welded pipes, API 5L welded pipes, spiral welded pipes, and large-diameter thick-walled straight seam steel pipes. The company has NM500 plate thickness size five production lines in three major production workshops: large-diameter longitudinally welded pipe production workshop,NM500 plate thickness size rolled steel pipe production workshop, and thermally expanded steel pipe production workshop, with an annual production capacity of more than 100,000 tons.

ASTM A514 steel is mainly used in places where high tensile strength and high yield are required, such as engineering vehicle lifting gears, large excavators, offshore platforms, etc. Different grades of A514 steel plate have different thickness, chemical composition and properties. However, the NM500 plate thickness size mechanical properties specified in ASTM A514 are similar to those of Q690 in China. A514 grade Q is generally used as the rack for offshore platform. Its hardness is between 230-390MPa, yield is greater than 630MPa, and tensile strength is more than 700MPa.

The main advantage of weather resistant steel plate is its weathering ability. When exposed to the atmosphere, the weather resistant steel plate will form a anti-corrosion film on the surface, and prevent further corrosion to the steel NM500 plate thickness size. Thus the weather resistant steel plate almost needs no paint treatment, which is the important measure for carbon steel plates to avoid going rust. Therefore, the maintance cost of weather resistant steel plate is low. The weather resistant steel plate is suitable for outside structure and construction use.

Since the welding process is often used in the fabrication and processing of steel structures, it is very important for low-alloy high-strength steels of such purpose to be welded using the arc welding process that is widely used in thin thickness plates and steel strips. Yes, the welding seam of the steel structure should have the required strength and toughness, so as to withstand the most unfavorable conditions for the intended use. At present, the development of NM500 plate thickness size, low-alloy high-strength steels is carried out simultaneously with the development of various welding processes. Most low-alloy high-strength steels can be welded well.

NM500 wear plate is Chinese abrasion resitant steel. NM500 steel is equivalent to AR500, HARDOX500, XAR500 and so on materials. The surface Brinell hardness of NM500 wear plate is ≥470 HBW. The NM500 steel is consists of max. 0.38% Carbon, 0.70 Silicon, 1.70 Manganese, 0.020 Phosphorus, 0.010 Sulfur, 1.20 Chrome, 1.00 Nickel, 0.65 Molybdenum, 0.050 Titanium, 0.0005-0.006 Boron, min. 0.010 Als, etc.. According to GBT24186, the max. thickness of NM500 plate thickness size, NM500 wear plate is 70mm.

Our company will accept the product quality objection registration record, pass it to the NM500 plate thickness size production unit and relevant departments, and timely coordinate the supervision of product NM500 plate thickness size quality objection. Our company coordinates the relevant department personnel to the customer unit to carry on the investigation, the processing.